Micromechanical modelling of interlaminar damage propagation and migration

L. F. Varandas, G. Catalanotti, A. Arteiro, António R. Melro, B. G. Falzon

Research output: Chapter in Book/Report/Conference proceedingChapter in a book

1 Citation (Scopus)

Abstract

Interlaminar crack onset and propagation in fibre-reinforced composites is here investigated in detail through the development of a micromechanics framework. The different dissipative effects that characterize crack propagation are assessed by using the appropriate constitutive material models. The phenomenon of delamination migration between angled plies is studied by embedding unit cells in-between homogenized plies. Different features associated with delamination migration are analyzed, such as the distribution of interlaminar shear stresses at the crack tip and the kink angles, aiding in the understanding of the complex phenomena linked to interlaminar crack migration. In addition, the influence of through-thickness compressive stress on the mode II interlaminar fracture toughness is studied and verified by comparing numerical predictions with experimental results, showing that the proposed computational framework represents a sound tool that can be used to better understand the micromechanics of interlaminar failure in advanced composite materials.

Original languageEnglish
Title of host publicationMulti-Scale Continuum Mechanics Modelling of Fibre-Reinforced Polymer Composites
PublisherElsevier
Pages307-347
Number of pages41
ISBN (Electronic)9780128189849
DOIs
Publication statusPublished - 1 Jan 2020

Bibliographical note

Publisher Copyright:
© 2021 Elsevier Ltd.

Keywords

  • Computational mechanics
  • Delamination migration
  • Finite element analysis
  • Fracture toughness
  • Interlaminar crack propagation
  • Polymer-matrix composites
  • Through-thickness compressive stress

Fingerprint

Dive into the research topics of 'Micromechanical modelling of interlaminar damage propagation and migration'. Together they form a unique fingerprint.

Cite this