Electrochemical modification and characterization of topological insulator single crystals

Research output: Contribution to journalArticle

Original languageEnglish
Number of pages14
Early online date29 Jan 2019
DateAccepted/In press - 29 Jan 2019
DateE-pub ahead of print (current) - 29 Jan 2019


We compare electrochemically modified or thiol functionalized single-crystal samples of the topological insulator (TI) Bi2Te0.9Se2.1 to freshly cleaved/air exposed control samples, and use X-ray photoelectron spectroscopy (XPS) to investigate the extent of any surface oxidation. XPS spectra for a TI sample maintained at an appropriate potential for 2 hours demonstrate the feasibility of protecting the TI surface from oxidation while working in an electrochemical environment. Deliberate electrochemical oxidation, in contrast, generates prominent Bi, Te and Se peaks associated with oxidation. However, this change is reversible, as further XPS spectra following electrochemical reduction are similar to those measured for an in-situ cleaved sample. XPS also shows that adsorption of pentanedithiol (PDT) protects the TI surface from oxidation. Cyclic voltammetry shows that PDT adsorption suppresses electrochemical oxidation and reduction, while electrochemical impedance spectroscopy shows that it increases the charge transfer resistance significantly. Our work demonstrate the ability to control and characterize the surface chemistry of single-crystal TIs in an electrochemical environment for the first time.

    Research areas

  • TOPOLOGICAL INSULATOR, Electrochemistry

Download statistics

No data available



  • Full-text PDF (accepted author manuscript)

    Rights statement: This is the author accepted manuscript (AAM). The final published version (version of record) is available online via ACS Publications at Please refer to any applicable terms of use of the publisher.

    Accepted author manuscript, 1.16 MB, PDF document


View research connections

Related faculties, schools or groups